W1A-2 is a grafted polymer of MAH, with polyolefin elastomer as the base material, with extremely low glass transition temperature characteristics and white and transparent particle appearance.
W1A-2 is a grafted polymer of MAH, with polyolefin elastomer as the base material, with extremely low glass transition temperature characteristics and white and transparent particle appearance.
The polyolefin elastomer used as the base material for W1A-2 is a type of synthetic rubber that is commonly used in applications that require flexibility and durability. By grafting MAH onto the polyolefin elastomer, the resulting polymer has improved properties, such as increased adhesion to other materials and enhanced compatibility with polar materials.
The extremely low glass transition temperature of W1A-2 means that it remains soft and flexible at low temperatures, making it ideal for use in applications where flexibility is essential, such as in seals, gaskets, and hoses. The white and transparent appearance of W1A-2 particles makes it useful in applications where clarity is important, such as in food packaging or medical devices.
W1A-2 is a grafted polymer of MAH, with polyolefin elastomer as the base material, with extremely low glass transition temperature characteristics and white and transparent particle appearance.
The resulting polymer has unique properties, including an extremely low glass transition temperature and a white, transparent particle appearance.
Characteristics | Value | Unit | Test Method |
Appearance | Granules | ||
Color | White | ||
Density | 0.87 | g/cm3 | ASTM D792 |
Melt Flow Rate(190℃2.16kg) | 0.3-1.0 | g/10min | ASTM D1238 |
Maleic Anhydride Content | High | wt% | COACE Method |
NOTE: The above data are typical test values and should not be interpreted as a specification low < 0.4wt %, medium 0.4-0.8 wt%, high > 0.8wt%
To be used as impact modifiers for PA6, PA66, and polyamide base fire retardant
compounds masterbatch.
To be used as compatibilizers to improve the compatibility between polyamide andpolypropylene, or polyethylene.
W1A-2 is a grafted polymer of maleic anhydride, with polyolefin elastomer as the base material, with extremely low glass transition temperature characteristics and white and transparent particle appearance.
View MoreModifier for Increasing The Impact Resistance and Processability of Nylon
View MorePolyolefin elastomer grafted maleic anhydride W1 is an internal antistatic agent widely used to polyolefin plastics such as PE, PP containers, drums (bags),(boxes), polypropylene spinning, non-woven fabrics. This product has good heat resistance, anti-static effect durable and efficient.
View MoreW1F with high flow properties that promotes separation of glass fibers scattered, reducing the impact on MI. Maleic anhydride functionalized polyolefin elastomer is a type of polymer that has been modified by the addition of maleic anhydride. This modification enhances the material's ability to adhere to other materials and promotes compatibility with other materials, making it useful in a wide range of applications.
View MoreCoace Chemical Company Limited
Colebond (xiamen) New Materials Co,.Ltd