Ultra-low temperature nylon toughener
W1B in the application of nylon + glass fiber modification, W1B can react with the glass fiber after surface treatment to improve the compatibility of nylon and glass fiber, thereby improving the tensile strength and impact strength of nylon.
The addition of the MA groups to the POE molecule introduces a strong polar side group, which can improve the adhesion and compatibility of the POE with non-polar materials. This is because the polar MA groups can interact with other polar molecules or surfaces, leading to improved bonding and compatibility.
W1B is commonly used in various applications, such as adhesives, coatings, and composites, where its polar nature can provide unique functional properties. In addition, the presence of the MA groups can also improve the thermal and mechanical properties of the material, making it a versatile and useful material for a range of applications.
W1B is prepared by grafting maleic anhydride by POE reaction. Since it introduces a strong polar side group (maleic anhydride) into the main chain of POE molecule, maleic anhydride grafted POE can become a polar material A bridge of adhesion and compatibility with non-polar materials.
W1B can be used both as a compatibilizer and as a toughening agent. As a nylon compatibilizer, it is also suitable for PA/PE, PA/PP alloys, which can improve the toughness of the alloy. W1B is an ultra-low temperature toughening agent. The impact strength of PA6+20%W1B at -40°C can be maintained at 70-80% of that at room temperature.
Characteristics | Value | Unit | Test Method |
Appearance | Pellets | ||
Color | White or light yellow | ||
Density | 0.87 | g/cm3 | ASTM D792 |
Melt Flow Rate(190℃2.16kg) | 0.3-2.0 | g/10min | ASTM D1238 |
Maleic Anhydride Content | High | wt% | COACE Method[1] |
Notes[1]LOW<0.4wt%; Middle(0.4wt%-0.8wt%); High≥0.8wt%.
1. Can be used as a compatibilizer for nylon and glass fiber;
2. Can be used as nylon toughening agent;
3. Can improve the adhesion between nylon and polar materials
W1A is prepared by grafting maleic anhydride by POE reaction.
View MoreIs ethylene elastomer with functionalized maleic anhydride, which is especially suitable for super-tough or cold-resistant nylon.
View MoreW1A is prepared by grafting maleic anhydride by POE reaction. Since it introduces a strongly polar side group (maleic anhydride) on the main chain of POE molecule, maleic anhydride grafted POE can become a polar material. A bridge for adhesion and compatibility with non-polar materials
View MoreModifier for Increasing The Impact Resistance and Processability of Nylon