Modifier for Increasing The Impact Resistance and Processability of Nylon
Test item | Test Data | Test Method |
Density | 0.87G/cm³ | ASTM D792 |
Melt flow rate(190℃/2.16kg) | 10-24g | ASTM D1238 |
Maleic anhydride content | High | COACE Method1 |
Moisture | ≤0.3% | Halogen Rapid Moisture Determination |
Appearance | Granular |
W1F is a maleic anhydride grafted polymer with a propylene elastomer copolymer as the matrix material, with very low glass transition temperature properties, high flow properties and a white translucent particle appearance.
W1F is a maleic anhydride functionalized polyolefin elastomer with high flow properties that promote glass fiber dispersion and reduce MI impact.
W1F is a maleic anhydride functionalized polyolefin elastomer that is often used as a coupling agent in reinforced polymer composites, such as those containing glass fibers. The maleic anhydride functionality on the W1F molecule can react with functional groups on the surface of the glass fibers, creating a stronger bond between the fibers and the polymer matrix.
In addition to its coupling agent properties, W1F also has high flow properties, which can help promote the dispersion of glass fibers in the polymer matrix during processing. This can result in improved mechanical properties of the composite material.
The statement that W1F can reduce MI (melt index) impact is somewhat unclear, as the impact resistance of a polymer is typically not directly related to its melt index. However, it is possible that the use of W1F as a coupling agent and flow promoter could lead to improvements in the impact resistance of a composite material containing glass fibers, due to better fiber dispersion and bonding.
1.Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance.
2.Be used for the compatibilizer of nylon and polypropylene/polyethylene alloy.
Be used for the macromolecular modifier(couling agent)of mineral-filled or grass-flber-filled nylon.
W1A-2 is a grafted polymer of maleic anhydride, with polyolefin elastomer as the base material, with extremely low glass transition temperature characteristics and white and transparent particle appearance.
View MoreW1B is prepared by grafting maleic anhydride by POE reaction.
View MoreIs ethylene elastomer with functionalized maleic anhydride, which is especially suitable for super-tough or cold-resistant nylon.
View MoreW1A is prepared by grafting maleic anhydride by POE reaction. Since it introduces a strongly polar side group (maleic anhydride) on the main chain of POE molecule, maleic anhydride grafted POE can become a polar material. A bridge for adhesion and compatibility with non-polar materials