High transparency and low crystal point silane-modified olefin copolymer photovoltaic encapsulation film glass adhesive
Performance | Numerical value | Test method(s) |
Density | 0.87g/cm³ | ASTM D792 |
Melt flow rate (190℃/2.16kg) | 10-20g/10min | ASTM D 1238 |
Silane content | High | COACE Method↿ |
Moisture | ≤0.3% | Halogen Rapid Moisture Determination |
Note:The above data are typical values tested and should not be interpreted as specification low < 0.4 wt %, medium 0.5-1.5 wt %, high > 1.5 wt %
R1020 is a silane-grafted POE film masterbatch for photovoltaic encapsulation. This product has the characteristics of high silane content, no precipitation, no water absorption, good dispersibility, good stability, high transparency, and good weather resistance.
The following data is derived from the average value of product retention sample testing within six months, and this data is updated every six months
Test item | Test data | Test method(s) |
Density | 0.87g/cm³ | ASTM D792 ISO 1183 |
Melting point | 46℃(115℉) | ASTM D3418 ISO 3146 |
Melting point | 15-20(190℃,2.16kg)g/10min | ASTM D1238 ISO 1133 |
Grafting rate | High | |
Appearance | transparent particles |
R1020 is a silane-modified olefin copolymer, which is mainly used in photovoltaic encapsulation films. It has the characteristics of high silane content, high transparency and low crystal point.
1. Photovoltaic packaging film
2. Glass adhesive
R1020 is a SIH4-grafted POE film masterbatch for photovoltaic encapsulation. This product has the characteristics of high SHI4 content, no precipitation, no water absorption, good dispersibility, good stability, high transparency, and good weather resistance.