Model No.: K2G
lntroduction:

Is a maleic anhydride grafted polymer with ethylene-vinyl acetate copolymer as matrix material


Test itemTest dataTest method
density0.94 g/cm³ASTM D792
Melt flow rate (190°C/2.16kg)15-30g/10minASTM D1238
Maleic anhydride contentHighColebond Method 1
moisture≤0.3 %Halogen Rapid Moisture Determination
AppearenceGranular
  • Description
  • Characteristic
  • Applications
  • Q& A
  • Related Product
  • Inquiry
Description

K2G is a general-purpose EVA-g-MAH product with excellent comprehensive properties.

EVA-g-MAH can be used as a film for hot-pressing bonding wood, and the bonding can be completed at a lower hot-pressing temperature. The following is Comparison table of bonding strength of EVA-g-MAH film to poplar board.

T-type peel strength test (aluminum sheet)
ModelT-peel strength N/25mm
EVA-VA28160
foreign competitors EVA-g-MAH258
K2G252
Figure 1: T-type test (aluminum sheet) standard parts and test process sketch

K2G-1

It can be seen from the above table that on the bonding metal aluminum, the adhesion of K2G is comparable to that of the American and foreign competitor EVA-g-MAH


K2G-2




Suggested dose:According to the actual application, taking into account the cost, the amount can be increased or decreased

Packaging, storage and transportation:20kg kraft bag with internal plastic bag. This product shall be treated as non-hazardous article and be stored or transported under dry conditions, and sunlight and rain shall be avoided.

Characterisitic

K2G is a maleic anhydride grafted polymer with ethylene-vinyl acetate copolymer as matrix material, which has strong adhesion to foil, paper and other polar substrates and has a white or yellowish transparent particle appearance.

Applications

It can be used as Hot melt adhesive for aluminum foil and polyester composite sheet and EVA alloy compatibilizer